HT (E.I.P.S) Carbon

Suitable for sweet wells with very low levels of H2S and CO2
  • The only UK manufacturer producing all of our Wirelines
    in our own ISO 9001 accredited factory.
  • All Wirelines exceed the requirements of API 9A
  • All Wirelines are 100% weld free
  • All Wirelines are supplied on painted steel reels
  • All lengths are available on request
  • All reels are packed with a unique protective wrap
    for secure transport
  • Wirelines are coated in custom developed inhibitors to
    further prevent corrosion resistance
  • Stock held in the UK and strategic locations worldwide

Do you require more information?

To receive more specific details about our HT (E.I.P.S) Carbon product range please click below or call:

+44 (0)121 772 2555

 

Click Here Now
Chemical Analysis
C Si Mn P S Cr Mo Cu Ni N
Weight % 0.9 Max 0.15 – 0.35 0.4 – 0.7 0.02 Max 0.025 Max 0.10 – Max 0.02 Max 0.10 Max 0.10 Max 0.007 Max
Mechanical Properties
Wireline Diameter (in) Minimum Breaking Load (lbf) Typical Breaking Load (lbf) Minimum UTS (N/mm²) Typical UTS (N/mm²) Yield Strength (0.2% of PS) Elastic Limit Modulus of Elasticity (N/mm²) Recommended Safe Load Sheave Diameter (in) Minimum Wraps
0.092″ 1830 1848 1600 1820 80% UTS 25% UTS 18 X 10′ 60% UTS 11 33
0.108″ 2490 2462 1590 1770 80% UTS 25% UTS 18 X 10′ 60% UTS 13 25
0.125″ 3300 3523 1590 1885 80% UTS 25% UTS 18 X 10′ 60% UTS 15 23
0.140″ 4200 3985 1570 1700 80% UTS 25% UTS 18 X 10′ 60% UTS 17 20
0.160″ 5500 5205 1570 1700 80% UTS 25% UTS 18 X 10′ 60% UTS 20 20
Physical Properties
Wireline Diameter Density (g/cm³) Coefficient of Liner Expansion (Mm/m/°C) Wireline Weight (lb/1000ft) Minimum Wireline Stretch (in/100ft/100lb) Thermal Conductivity (W/m.K) Specific Heat (j/kg.K) Resistivity (Ohm Cm) Magnetic Permeability
0.092″ 7.87 0.11 22.66 0.70 50 532 17 2420
0.108″ 7.87 0.11 31.23 0.51 50 532 17 2420
0.125″ 7.87 0.11 41.84 0.38 50 532 17 2420
0.140″ 7.87 0.11 52.41 0.307 50 532 17 2420
0.160″ 7.87 0.11 68.45 0.236 50 532 17 2420
Corrosion Resistance
H2S + CO² Very poor, may be used in very low H²S (1-2ppm) + CO² (2-3%) with inhibitors
Chloride (Brine, salt etc.) Good – wire must be cleaned after use to prevent pitting
H2S + CO²‚ + Chloride Extremely poor due to the presence of H²S + CO²